| General | ||||
|
Material Status
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.49
|
g/cm3
|
ASTM D792 |
|
Molding Shrinkage - Flow (3.20 mm)
|
0.50 to 1.1
|
%
|
ASTM D955 |
|
Water Absorption (24 hr, 23°C, 50% RH)
|
0.90
|
%
|
ASTM D570 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
121
|
|
ASTM D785 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 1 (Break, 3.20 mm)
|
127
|
MPa
|
ASTM D638 |
|
Tensile Elongation 1 (Break, 3.20 mm)
|
4.0
|
%
|
ASTM D638 |
|
Flexural Modulus 2 (3.20 mm)
|
7350
|
MPa
|
ASTM D790 |
|
Flexural Strength 2 (3.20 mm)
|
196
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.20 mm)
|
59
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
200
|
°C
|
ASTM D648 |
|
Peak Melting Temperature
|
220
|
°C
|
ASTM D3418 |
|
CLTE - Flow
|
4.0E-5
|
cm/cm/°C
|
ASTM D696 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Volume Resistivity (23°C)
|
1.0E+17
|
ohms·cm
|
ASTM D257 |
|
Dielectric Strength (23°C, 1.00 mm)
|
21
|
kV/mm
|
ASTM D149 |
|
Dielectric Constant (23°C, 1.00 GHz)
|
3.00
|
|
ASTM D150 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80 to 100
|
°C
|
|
|
Drying Time
|
4.0 to 5.0
|
hr
|
|
|
Suggested Max Moisture
|
< 0.10
|
%
|
|
|
Rear Temperature
|
245 to 265
|
°C
|
|
|
Middle Temperature
|
255 to 280
|
°C
|
|
|
Front Temperature
|
255 to 285
|
°C
|
|
|
Nozzle Temperature
|
255 to 285
|
°C
|
|
|
Processing (Melt) Temp
|
255 to 285
|
°C
|
|
|
Mold Temperature
|
80 to 100
|
°C
|
|
|
Screw Speed
|
50 to 150
|
rpm
|