| General | ||||
|
Material Status
|
|
|||
|
UL Yellow Card 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.18
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
15
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow (3.20 mm)
|
0.40 to 0.60
|
%
|
ASTM D955 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (Yield)
|
61.3
|
MPa
|
ASTM D638 |
|
Tensile Elongation 2 (Break)
|
> 60
|
%
|
ASTM D638 |
|
Flexural Modulus 3 (3.20 mm)
|
2600
|
MPa
|
ASTM D790 |
|
Flexural Strength 3 (3.20 mm)
|
95.1
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.20 mm)
|
590
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm)
|
92.0
|
°C
|
ASTM D648 |
|
Vicat Softening Temperature
|
97.0
|
°C
|
ASTM D1525 4 |
|
RTI Elec
|
60.0
|
°C
|
UL 746B |
|
RTI Imp
|
60.0
|
°C
|
UL 746B |
|
RTI Str
|
60.0
|
°C
|
UL 746B |
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.9 mm
|
V-0
|
|
|
|
1.0 mm
|
V-0
|
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80 to 90
|
°C
|
|
|
Drying Time
|
3.0 to 5.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Rear Temperature
|
220 to 255
|
°C
|
|
|
Middle Temperature
|
220 to 275
|
°C
|
|
|
Front Temperature
|
245 to 275
|
°C
|
|
|
Nozzle Temperature
|
245 to 275
|
°C
|
|
|
Processing (Melt) Temp
|
245 to 275
|
°C
|
|
|
Mold Temperature
|
60 to 80
|
°C
|
|
|
Screw Speed
|
40 to 70
|
rpm
|