| General | ||||
|
Material Status
|
|
|||
|
UL Yellow Card 1
|
|
|||
|
Search for UL Yellow Card
|
|
|||
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.19
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR)
|
|||
|
250°C/2.16 kg
|
15
|
g/10 min
|
ASTM D1238 |
|
250°C/2.16 kg
|
|
g/10 min
|
ISO 1133 |
|
Molding Shrinkage - Flow (3.20 mm)
|
0.40 to 0.60
|
%
|
ASTM D955, ISO 294-4 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
|||
|
Yield 2
|
62.8
|
MPa
|
ASTM D638 |
|
Yield
|
60.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation
|
|||
|
Break 2
|
> 80
|
%
|
ASTM D638 |
|
Break
|
100
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
3.20 mm 3
|
2650
|
MPa
|
ASTM D790 |
|
-- 4
|
2500
|
MPa
|
ISO 178 |
|
Flexural Strength
|
|||
|
3.20 mm 3
|
93.2
|
MPa
|
ASTM D790 |
|
-- 4
|
95.0
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | ||
|
-30°C
|
40
|
kJ/m2
|
|
|
23°C
|
45
|
kJ/m2
|
|
|
Notched Izod Impact (23°C, 3.20 mm)
|
610
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 6.40 mm
|
103
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed
|
87.0
|
°C
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
100
|
°C
|
ISO 306/B50 |
|
RTI Elec
|
80.0
|
°C
|
UL 746B |
|
RTI Imp
|
80.0
|
°C
|
UL 746B |
|
RTI Str
|
85.0
|
°C
|
UL 746B |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Comparative Tracking Index (Solution A)
|
250
|
V
|
IEC 60112 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
1.2 mm
|
V-0
|
|
|
|
3.0 mm
|
V-0
|
|
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
75 to 85
|
°C
|
|
|
Drying Time
|
3.0 to 5.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Rear Temperature
|
220 to 240
|
°C
|
|
|
Middle Temperature
|
235 to 255
|
°C
|
|
|
Front Temperature
|
250 to 265
|
°C
|
|
|
Nozzle Temperature
|
250 to 265
|
°C
|
|
|
Processing (Melt) Temp
|
235 to 265
|
°C
|
|
|
Mold Temperature
|
50 to 80
|
°C
|
|
|
Screw Speed
|
40 to 70
|
rpm
|